Self lubricating fiber composite material wrapped bearing

GXT-60 linear pulley bearing

Features: low friction coefficient, high load-bearing capacity, resistance to different axial degrees, wear resistance, low water absorption, corrosion resistance, impact resistance

structure

Wear resistant layer: PTFE and high-strength fiber pre woven fabric, unique weaving design, the inner surface of the product presents a concave convex structure, reducing the contact area between the product and the pin shaft. The friction coefficient is the lowest among the tension series products. It is suitable for testing and practical application in situations where low friction coefficient is required, such as linear motion and pulley components, without jerking and anti abnormal noise.

Substrate: Glass fiber and epoxy resin cured body, giving it the same compressive performance as GMM and others.

Application: Recommended use of straight lines and guide wheels

Mechanical and physical performance unit values

Ultimate compressive strength MPa 513

Maximum load (static) MPa 310

Maximum load (dynamic) MPa 207

Temperature range ° C -1980-163

Thermal expansion coefficient m/m/° C 8.69x10-6

Thermal conductivity W/m-k 0.26-0.33

Water absorption rate of 0.12% in 2 hours

Water absorption rate of 0.16% in 24 hours

Density g/cm3 1.75-1.95

The maximum speed of dry running application is m/s 0.25

Maximum PV value N/mm2 x m/s 1.55

Friction coefficient f 0.05-0.08

Typical average design pressure for high proportion applications MPa 69

Wear after 500000 cycles mm<0.15